钢模具的需求量在不断增加
隔离墩钢模具是生产水泥制品的钢模具,这种模具的生产工艺比较简单,可以选用塑料模具生产,也可以选用钢模具生产,模具的尺寸规格比较大,选用钢模具生产具有一定的优势, 现在模具市场竞争越来越激烈,客户订货的时候也会咨询几家进行比较,未来的模具市场也是越来越难做。国家大力建设高速,高铁,每年水泥隔离墩钢模具的需求量也在不断增加。
Isolation pier steel mold is a steel mold for cement products. The production process of this kind of mold is relatively simple. Plastic mold can be used for production or steel mold can be used for production. The size and specification of the mold are relatively large. It has certain advantages to select steel mold for production. Now the market competition of the mold is becoming more and more fierce, and customers will consult several for comparison when ordering. The future mold market is also the same. It's getting harder and harder to do. The state vigorously builds high-speed and high-speed railway, and the demand of steel mould for cement isolation pier is increasing every year.
隔离墩钢模具冷却与润滑为减轻模具的热负荷,避免模具温度过高,通常在钢模具工作的间歇对其进行强制性冷却,由此造成模具周期性的激热、激冷作用将会产生热疲劳裂纹。因此,钢模具使用结束后应缓慢冷却,否则将会出现热应力,从而引起模具的开裂失效。H13钢模具工作时可采用石墨含量为12%的水基石墨进行润滑,降低成形力,保证金属在型腔中正常流动和锻件顺利脱模;此外,石墨润滑剂还具有散热作用,可以降低H13钢模具的工作温度。
In order to reduce the heat load of the die and avoid the excessive temperature of the die, the cooling and lubrication of the steel die for isolation pier are usually forced to cool the die during the intermission of the work of the die. Thermal fatigue cracks will occur due to the periodic heating and cooling action of the die. Therefore, the steel die should be cooled slowly after use, otherwise thermal stress will occur, which will lead to cracking failure of the die. The water-based graphite with 12% graphite content can be used to lubricate the H13 steel die to reduce the forming force and ensure the normal flow of metal in the cavity and the smooth demoulding of forgings. In addition, the graphite lubricant also has the function of heat dissipation, which can reduce the working temperature of the H13 steel die.
隔离墩钢模具进行养护的时候,我们需要将存储的钢模具进行有效的保管,一般都是室内存储效果更佳。模具进行养护的时间周期一般控制在每天进行,维修的时间控制在每10-30天左右进行一次,应为长时间,长频率的使用,会给隔离墩钢模具带来一定的磨损情况,所以我们要在有效的时间内,进行标准的检测。
When the steel mould of isolation pier is maintained, we need to keep the stored steel mould yamocao.37ix.com.cnqizhong.37ix.com.cnzhushe.37ix.com.cngeshengban.89ix.comeffectively. tongfoxiang.71ix.comboligangjg.37ix.com.cnGenerally, the indoor storage effect is better. The time period of mould maintenance is generally controlled every day, and the time of maintenance is controlled every 10-30 days or so. It should be used for a long time and a long frequency, which will bring certain wear and tear to the isolation pier steel mould. Therefore, we need to carry out standard testing in an effective time.
Isolation pier steel mold is a steel mold for cement products. The production process of this kind of mold is relatively simple. Plastic mold can be used for production or steel mold can be used for production. The size and specification of the mold are relatively large. It has certain advantages to select steel mold for production. Now the market competition of the mold is becoming more and more fierce, and customers will consult several for comparison when ordering. The future mold market is also the same. It's getting harder and harder to do. The state vigorously builds high-speed and high-speed railway, and the demand of steel mould for cement isolation pier is increasing every year.
隔离墩钢模具冷却与润滑为减轻模具的热负荷,避免模具温度过高,通常在钢模具工作的间歇对其进行强制性冷却,由此造成模具周期性的激热、激冷作用将会产生热疲劳裂纹。因此,钢模具使用结束后应缓慢冷却,否则将会出现热应力,从而引起模具的开裂失效。H13钢模具工作时可采用石墨含量为12%的水基石墨进行润滑,降低成形力,保证金属在型腔中正常流动和锻件顺利脱模;此外,石墨润滑剂还具有散热作用,可以降低H13钢模具的工作温度。
In order to reduce the heat load of the die and avoid the excessive temperature of the die, the cooling and lubrication of the steel die for isolation pier are usually forced to cool the die during the intermission of the work of the die. Thermal fatigue cracks will occur due to the periodic heating and cooling action of the die. Therefore, the steel die should be cooled slowly after use, otherwise thermal stress will occur, which will lead to cracking failure of the die. The water-based graphite with 12% graphite content can be used to lubricate the H13 steel die to reduce the forming force and ensure the normal flow of metal in the cavity and the smooth demoulding of forgings. In addition, the graphite lubricant also has the function of heat dissipation, which can reduce the working temperature of the H13 steel die.
隔离墩钢模具进行养护的时候,我们需要将存储的钢模具进行有效的保管,一般都是室内存储效果更佳。模具进行养护的时间周期一般控制在每天进行,维修的时间控制在每10-30天左右进行一次,应为长时间,长频率的使用,会给隔离墩钢模具带来一定的磨损情况,所以我们要在有效的时间内,进行标准的检测。
When the steel mould of isolation pier is maintained, we need to keep the stored steel mould yamocao.37ix.com.cnqizhong.37ix.com.cnzhushe.37ix.com.cngeshengban.89ix.comeffectively. tongfoxiang.71ix.comboligangjg.37ix.com.cnGenerally, the indoor storage effect is better. The time period of mould maintenance is generally controlled every day, and the time of maintenance is controlled every 10-30 days or so. It should be used for a long time and a long frequency, which will bring certain wear and tear to the isolation pier steel mould. Therefore, we need to carry out standard testing in an effective time.